2752(2751)硅橡膠玻璃纖維軟管
詳細說明：SRG-502
2752(2751)硅橡膠玻璃纖維軟管(符合滬Q/JBQR5-2000)
2752(2751) Fiberglass Sleeving coated With Silicone Rubber (In According With Shanghai Q/JBQR5-2000)
硅橡膠玻璃纖維軟管是由無堿玻璃纖維編織成套管，然后涂以硅橡膠，經(jīng)加熱硫化而成的絕緣套管。本產(chǎn)品具有一定的介電性能，較高的耐熱性、優(yōu)良的耐寒性和富于彈性，適用于H級絕緣電機、電器的布線絕緣和機械保護。
注：內(nèi)徑1.5毫米及以下的軟管，擊穿電壓不得低于規(guī)定值的75%。
Fiberglass sleeving coated with silicone rubber produced with the process of thermal treatment and vulcanization is the non-alkli fiberglass braided sleeving coated with silicone rubber.This sleeving possesses good qualities of dielectric,high temperature resistace,excellent elasticity and cold resistance.It can be used for wiring insulation and mechanical protection for H grade electrical appliances.
Note:The breakdown voltage for sleevings whose inner diameter is or be low1.5mm should not than 75% of the specified voltage.
內(nèi)徑(mm)
Inner Diametor | 壁厚(mm)
Wall Thickness |
標稱
Nominal | 公差
Tolerance | 標稱
Nominal | 公差
Tolerance |
1；1.5 | +0.20/-0.10 | 0.40 | ±0.10 |
2；2.5；3；3.5 | +0.30/-0.10 | 0.50 | ±0.15 |
4；5；6 | +0.40/-0.20 | 0.60 | ±0.20 |
7；8；9 | +0.50/-0.30 | 0.70 | ±0.20 |
10；11；12 | +0.80/-0.50 | 0.80 | ±0.20 |
14；16；18；20；23；27；28 | +1.00/-1.00 | 1.00 | ±0.30 |
性能指標 Property requirements |
性能Property | 指標Requirements |
彈性
Elasticity | 膠膜不應于玻璃絲管脫開或產(chǎn)生開裂
No cracking or detachment of coating shall be visible.
①200±2℃處理3小時
After 3 hours at 200±2℃
②-40～60℃處理2小時
After 2 hours at -40～60℃ |
耐燃性
Flame resistance | 不小于45秒/25毫米
Not less than 45sec./25mm |
耐熱性
Heat resistance | 200±5℃處理72小時后膠膜不應與玻璃絲管脫開或產(chǎn)生開裂
No cracking detachment of coating shall be visible after 72 hours at 200±5℃ |
擊穿電壓千伏、大于
Breakdown voltage kv,min | 室溫時 4.0
At room temp 4.0 |
受潮時 2.0
After damp 2.0 |